Valentine White Earthenware Powdered Clay
Traditional white burning body containing ball clay, China clay, flint, and flux. Ideal for casting small to medium items with good glaze fit. Also ideal for making your own decorating slips.
- Temperature Range 1060°C - 1100°C.
- Shrinkage (w-f) 2-4%.
- Shrinkage (d-f) 6 - 8%
- 0.37% expansion at 500°C.
- Texture (1-smooth10-coarse) 1.
- Fired colour: White.
- 20kg bag.
White Earthenware Powder Casting Slip Recipe:
- P3100 White Earthenware Powder Clay - 50kg.
- Water – 20 Litre.
- P3342 Soda Ash - 17gm.
- P3344 Soda Sil - 51gm.
Weight (kg)
Pickup available at Stoke-on-Trent
Usually ready in 2-4 days
Valentine White Earthenware Powdered Clay
20
Stoke-on-Trent
Pickup available, usually ready in 2-4 days
Campbell Road
Stoke-on-Trent ST4 4ET
United Kingdom
Traditional white burning body containing ball clay, China clay, flint, and flux. Ideal for casting small to medium items with good glaze fit. Also ideal for making your own decorating slips.
- Temperature Range 1060°C - 1100°C.
- Shrinkage (w-f) 2-4%.
- Shrinkage (d-f) 6 - 8%
- 0.37% expansion at 500°C.
- Texture (1-smooth10-coarse) 1.
- Fired colour: White.
- 20kg bag.
White Earthenware Powder Casting Slip Recipe:
- P3100 White Earthenware Powder Clay - 50kg.
- Water – 20 Litre.
- P3342 Soda Ash - 17gm.
- P3344 Soda Sil - 51gm.
Clay Fired Colour | White |
---|---|
Clay Texture | Smooth |
Clay Firing Temperature Range | 1060-1100 |
Safety data sheet | See |
- A potter and sculptors favourite place to shop for over 40 years. We have everything you need!
- A wide and relevant product range with fantastic stock availability!
- Our prices are transparent and competitive!
- Expert technical advice with every purchase!
“Pottery is not just about shaping clay, it's a dance between the hands and the earth, a symphony of creation.
“Pottery is not just about shaping clay, it's a dance between the hands and the earth, a symphony of creation.
“Pottery is not just about shaping clay, it's a dance between the hands and the earth, a symphony of creation.